| Place of Origin: | Japan |
| Brand Name: | SKYWELL |
| Certification: | SGS |
| Model Number: | T700SC-12000-50C |
| Minimum Order Quantity: | 10 m2 |
|---|---|
| Price: | USD4-6 per m2 |
| Packaging Details: | Box size 110*35*35CM |
| Delivery Time: | 2-3 days |
| Payment Terms: | L/C, , T/T, Western Union,Paypal |
| Supply Ability: | 100000 m2 per month |
| Carbon Fiber: | Toray T700SC-12000-50C | FAW (fiber Content [g/m2: | 75 |
|---|---|---|---|
| Resin Content [g/m2: | 37 | Twist: | No Twist |
| Resin System: | Epoxy | Curing Temperature: | 125 Celsius |
| Tensile Strength Mpa [kgf/mm2]: | 5410 | Tensile Modulus [GPa[10³ Kgf/mm2]: | 233 |
| Elongation: | 2.3% | Density [10³kg/m³]: | 2 |
| YIELD: | 809 | Process: | Filament Winding - Pultrusion - Prepreg |
| Typical Applications: | Motorsport, Sport & Leisure, Industrial | ||
| High Light: | polypropylene spunbond nonwoven fabric,meltblown nonwoven fabric |
||
Unidirectional Carbon fibe prepreg T700SC-12000-50C and epoxy resin system high Modulus 233GPa
We provide carbon fiber prepregs, including UD prepregs (in which carbon fibers are unidirectionally stretched and impregnated with resin) and cross prepregs (that is, carbon fiber woven cloth impregnated with resin).
Ultra-high modulus PAN carbon fiber is widely used as a material for manufacturing automobiles and sports products. Other applications include construction/civil engineering and aerospace industry.
It can be impregnated with epoxy resin according to customer requirements, and it is developed assuming use in different high temperature ranges. Using this prepreg can expand the application range of the product.
Specification:
| Resin system | Epoxy |
| Tensile Strength | 710.7 KSI |
| Tensile Modulus | 33.4 MSI |
| Elongation | 2.3% |
| Denisty | 0.065 lb/in³ |
| Filament diameter | 0.28 mil |
| Resin | Epoxy |
| Size content | 1% |
| Precursor | Pan |
| K | 12k |
| Twisted | Never |
| Tow Size | Small tow |
| Cross sectional area | 68.2[in2.10³] |
| Resistivity (23 Celsius) | 630 x10-6 [Ω.in] |
Application: